Reductive Fractionation of Flax Shives in Ethanol Medium over RuNi Bimetallic Catalysts.

The reductive catalytic fractionation of flax shives in the presence of bimetallic NiRu catalysts supported on oxidized carbon materials (CM) such as mesoporous Sibunit and carbon mesostructured by KAIST (CMK-3) was studied. The catalysts based on CMK-3 were characterized by a higher surface area (1216 m2/g) compared to the ones based on Sibunit (315 m2/g). The catalyst supported on CMK-3 (10Ni3RuC400) was characterized by a more uniform distribution of Ni particles, in contrast to the Sibunit-based catalyst (10Ni3RuS450), on the surface of which large agglomerated particles (300-400 nm) were presented. The bimetallic catalysts were found to be more selective towards propanol-substituted methoxyphenols compared to monometallic Ru/C and Ni/C catalysts. A high yield of monomers (up to 26 wt%, including 17% 4-propanol guaiacol) was obtained in the presence of a 10Ni3RuC400 catalyst based on CMK-3.

Larix Sibirica Arabinogalactan Hydrolysis over Zr-SBA-15; Depolymerization Insight.

Arabinogalactan depolymerization over solid Zr-containing SBA-15-based catalyst was studied via HPLC, GPC, and theoretical modeling. Arabinogalactans (AG) are hemicelluloses mainly present in larch wood species, which can be extracted on an industrial scale. The application of solid acid catalysts in the processes of hemicellulose conversion can exclude serious drawbacks such as equipment corrosion, etc. Characterization of 5%Zr-SBA-15 confirmed the successful formation of the mesoporous structure inherent to SBA-15 with fine Zr distribution and strong acidic properties (XRD, XPS, FTIR, pHpzc). Carrying out the process at 130 °C allowed us to achieve total products yield of up to 59 wt%, which is represented mainly by galactose (51 wt%) and minor (less than 9 wt%) presence of arabinose, furfural, 5-HMF, and levulinic acid. The temperature increases up to 150 °C resulted in a total product yield drop down to 37 wt%, making temperature elevation above 130 °C obsolete. According to the theoretical investigations, arabinogalactan depolymerization follows the primary cleavage of the ß(1→3) bonds between the D-galactose units of the main chain, which is also confirmed by GPC.